UNCURED

TSE2186U

Appearance

Dark gray

Specific Gravity (23°C)

1.49

Williams Plasticity

210

CURED COMPOUND (Press cure 10min  170°C; Post cure 4hrs   200°C; TC-8 curing agent 0.5phc)

MECHANICAL PROPERTIES(JIS K6249)

Hardness (Type A)

58

Tensile Strength        MPa {kgf/cm²}

8.0{82}

Elongation             %

350

Tear Strength (Angle)   N/mm{kgf/cm}

21{21}

Compression Set^*1) %

8

Linear Shrinkage %

3.6

ELECTRICAL PROPERTIES (JIS K6249)

Dielectric Strength      kV/mm

23

Volume Resistivity MW·m{W·cm}

6×10⁷{6×10¹⁵}

1) After aging 22hrs   180°C